OLA T1500(LCD-RESIN)

3D Printing LCD Resin Black
More Details

This revolutionary elastic engineering resin combines polypropylene's toughness with engineering plastic's strength for unprecedented performance. PP-like flexibility, Excellent impact resistance, Unique stiffness-flexibility balance


  • Thermal Properties
    Heat Deflection Temperature @0.45MPa: 66℃
    Heat Deflection Temperature @1.82MPa: 53℃

  • Mechanical Properties
    Tensile Modulus: 1.46 GPa
    Tensile Strength: 34 MPa
    Elongation at Break: 155%
    Flexural Modulus: 1.37 GPa
    Flexural Strength: 41 MPa
    Notched Impact Strength: 42 J/m
    Unnotched Impact Strength: 910 J/m


Max. Part Size:

200mm x 125mm x 210mm

Tolerance and Precision：

±100 µm or ±0.1%


View Data Sheet

OLA T2000(LCD-RESIN)

3D Printing LCD Resin Gray-black
More Details

This ABS-like engineering resin combines strength with toughness, ideal for functional parts requiring long-term stability.

  • Thermal Properties

    Heat Deflection Temperature (HDT @ 0.45MPa): 53°C

    Heat Deflection Temperature (HDT @ 1.82MPa): 63°C

  • Mechanical Properties

    Tensile Modulus (ASTM D 638): 2.2 GPa

    Tensile Strength (ASTM D 638): 46 MPa

    Elongation at Break (ASTM D 638): 48%

    Flexural Modulus (ASTM D 790): 1.9 GPa

    Flexural Strength (ASTM D 790): 65 MPa

    IZOD Impact Strength (ASTM D 256): 40 J/m

    Notched IZOD Impact Strength (ASTM D 4812): 715 J/m

Max. Part Size:

200mm x 125mm x 210mm

Tolerance and Precision：

±100 µm or ±0.1%


View Data Sheet

OLA Flame-Retardant Resin(LCD-RESIN)

3D Printing LCD Resin Gray
More Details

This professional halogen-free material combines safety and mechanical performance for demanding applications.UL 94 V-0 rated, Excellent heat resistance, Professional surface finish

  • Thermal Properties

    Heat Deflection Temperature (HDT @1.8MPa): 71℃

    Heat Deflection Temperature (HDT @0.45MPa): 94℃

    Coefficient of Thermal Expansion (ASTM E 813-13, 20-80℃): 98.6μm/m/°C

    Glass Transition Temperature (Peak tan δ, heating rate: 3℃pm): 130℃

  • Mechanical Properties

    Elongation at Break (ASTM D638-14): 9.4%

    Tensile Modulus (ASTM D638-14): 2.94 GPa

    Ultimate Tensile Strength (ASTM D638-14): 38 MPa

    Flexural Modulus (ASTM D790-15): 2.7 GPa

    Flexural Strength (ASTM D790-15): 72 MPa

    IZOD Impact Strength (ASTM D256-10): 22 J/m

    Maximum Stress Intensity Factor (Kmax): 1.05 MPa · m1/2

    Fracture Work (Wf): 311 J/m²

    Hardness (ASTM D2240): 80D

  • Electrical Properties

    Viscosity (25℃): 4500-5000 cp

    Dielectric Strength (ASTM D 149): 15.1 kV/mm

    Dielectric Constant (ASTM D150, 0.5 MHz): 3.83

    Dielectric Constant (ASTM D150, 1.0 MHz): 3.82

    Dissipation Factor (ASTM D150, 0.5 MHz): 0.024

    Dissipation Factor (ASTM D150, 1.0 MHz): 0.025

    Volume Resistivity (ASTM D257): [Data Not Provided]

Max. Part Size:

200mm x 125mm x 210mm

Tolerance and Precision：

±150 µm or ±0.15%


View Data Sheet

OLA ESD Anti-Static Resin(LCD-RESIN)

3D Printing LCD Resin Black
More Details

Specially developed for electronics manufacturing to protect sensitive components from electrostatic damage.Professional ESD protection, Excellent mechanical strength, Cost-effective

  • Thermal Properties

    Heat Deflection Temperature (HDT @1.8MPa): 54.2℃

    Heat Deflection Temperature (HDT @0.45MPa): 62.2℃

    Coefficient of Thermal Expansion (ASTM E 813-13): 123.7 μm/m/°C

  • Mechanical Properties

    Elongation at Break (ASTM D638-14): 12%

    Tensile Modulus (ASTM D638-14): 1.937 GPa

    Ultimate Tensile Strength (ASTM D638-14): 44.2 MPa

    Flexural Modulus (ASTM D790-17): 1.841 GPa

    Flexural Strength (ASTM D790-17): 61 MPa

    IZOD Impact Strength (ASTM D256-10): 26 J/m

    Shore Hardness (ASTM D2240): 90D

  • Electrical Properties

    Surface Resistivity (ANSI/ESD11.11): See attachment

    Volume Resistivity (ANSI/ESD11.11): See attachment

Max. Part Size:

200mm x 125mm x 210mm

Tolerance and Precision：

±150 µm or ±0.15%


View Data Sheet

OLA8600Pro(LCD-RESIN)

3D Printing LCD Resin Gray
More Details

This versatile resin delivers the perfect balance between precision, aesthetics and strength for premium models and functional verification.Exhibition-grade finish, Outstanding mechanical properties, Ultra-high precision

  • Thermal Properties

    Heat Deflection Temperature (HDT @1.8MPa): 59℃

    Heat Deflection Temperature (HDT @0.45MPa): 71℃

  • Mechanical Properties

    Elongation at Break (ASTM D638-14): 13%

    Tensile Modulus (ASTM D638-14): 2.675 GPa

    Ultimate Tensile Strength (ASTM D638-14): 62 MPa

    Flexural Modulus (ASTM D790-15): 2.75 GPa

    Flexural Strength (ASTM D790-15): 103 MPa

    IZOD Impact Strength (ASTM D256-10): 32 J/m

Max. Part Size:

200mm x 125mm x 210mm

Tolerance and Precision：

±100 µm or ±0.1%


View Data Sheet

OLA RedWaxPro(LCD-RESIN)

3D Printing LCD Resin Orange
More Details

This professional resin is specially developed for precision casting and detailed modeling applications. Ultra-high detail resolution, Mirror-like finish, Industrial-grade performance

  • Thermal Properties

    Heat Deflection Temperature: 63℃

  • Mechanical Properties

    Tensile Strength: 40-58 MPa

    Tensile Modulus: 2511-2665 MPa

    Elongation at Break: 11-16%

    Flexural Strength: 71-76 MPa

    Flexural Modulus: 2495-2565 MPa

    Shore Hardness: 88

    Notched Impact Strength: 30-40 J/m

  • Other Properties

    Coefficient of Thermal Expansion: 92

    Dielectric Constant (60 Hz): 4.5

Max. Part Size:

192mm x 108mm x 200mm

Tolerance and Precision：

±100 µm or ±0.1%


View Data Sheet

OLA3280 Ceramic Resin(LCD-RESIN)

3D Printing LCD Resin White
More Details

OLA 3280 is a high-glass-content resin with ceramic-like properties, engineered for demanding industrial applications. Smooth matte surface, Extreme hardness, Excellent heat resistance, Superior chemical resistance

  • Thermal Properties

    Heat Deflection Temperature (0.45MPa): 163℃

    Heat Deflection Temperature (1.82MPa): 82℃

  • Mechanical Properties

    Tensile Strength (ASTM D638): 65 MPa

    Tensile Modulus (ASTM D638): 10 GPa

    Elongation at Break (ASTM D638): 1%

    Flexural Strength (ASTM D790): 126 MPa

    Flexural Modulus (ASTM D790): 9 GPa

    IZOD Impact Strength (ASTM D256): 16 J/m

  • Other Properties

    Shore Hardness (ASTM D2240): 90D

Max. Part Size:

200mm x 125mm x 210mm

Tolerance and Precision：

±100 µm or ±0.1%


View Data Sheet

OLA 5100 PEEK(FDM-PEEK)

180$

FDM PEEK Light Yellow
More Details

PEEK 3D printing material is highly sought after in the medical industry due to its excellent biocompatibility and ability to be sterilized, making it ideal for custom medical implants. Additionally, its outstanding wear resistance and high-temperature stability make it a preferred material for producing aerospace parts and automotive components that require superior durability and thermal performance.


  • Thermal Properties
    Heat Deflection Temperature (ISO 75-1-2020): 280 °C (0.45 MPa), 155 °C (1.82 MPa)
    Melting Point: 343 °C

  • Mechanical Properties
    Tensile Modulus (ISO 527-1-2019): 3.5 GPa
    Tensile Strength (ISO 527-1-2019): 78 MPa
    Elongation at Break (ISO 527-2018): 2.5 %

  • Other Features
    Excellent chemical, oil, and heat resistance


Max. Part Size:

180mm x 180mm x 200mm

Tolerance and Precision：

±300μm or ±0.3%


View Data Sheet
All Materials

OLA 3D Printing Service Platform

Get instant quote
Copyright © 2023 OLA 3D Printing All rights reserved.