OLA 7100Pro is a cost-effective nylon-like PA12 SLS material offering excellent mechanical properties and durability. It’s engineered for long-term usage, with high dimensional stability and consistent strength across all directions. Compared to traditional PA12, 7100Pro provides similar performance at a significantly lower cost, making it one of the most economical and widely applicable SLS materials on the market.
Mechanical Properties
Tensile Strength (ISO527-1:2019): 42 MPa (X/Y)
Tensile Modulus (ISO527-1:2019): 1450 MPa (X/Y)
Elongation at Break (ISO527-1:2018): 40% (X/Y)
Bending Strength (GB/T 9341-2008): 48 MPa (X/Y)
Bending Modulus (GB/T 9341-2008): 1400 MPa (X/Y)
Thermal Properties
Heat Deflection Temperature (HDT @ 1.8 MPa): 52°C
Heat Deflection Temperature (HDT @ 0.45 MPa): 145°C
Melting Point (10°C/min): 185.5°C
Impact Properties
Notched Impact Strength (GB/T 1843-2008): 10 kJ/m² (X/Y)
Unnotched Impact Strength (GB/T 1843-2008): 32 kJ/m² (X/Y)
Max. Part Size:
350mm × 350mm × 400mm
Tolerance and Precision：
±300 μm or ±0.3%